厂商 ：天津中天俊达玻纤制品有限公司
天津 天津- 主营产品：
联系电话 ：13512972377
商品详细描述
1) 产品特性和用途
高硅氧玻璃纤维布具有强度高、易加工、用途广的特点，用作耐高温、耐烧蚀、隔热、保温材料。产品厚度0.1mm-1.5mm，并可根据用户要求进行表面涂覆处理等。
(2) 产品技术指标
产品代号 公称厚度 mm 宽度 cm SiO2含量 % 热失量 % 组织
BWT100 0.10 80~90 ≥96 ≤3 平纹
BWT260 0.26 平纹
BWT600 0.72 80~1200 缎纹
BWT1250 1.35 缎纹
? SiO2≥96%
? Soft point nearly 1700℃, long-period service at 900℃
? Low thermal conductivity
? Good chemical stability
? Good electrical insulation
? Low thermal shrinkage
? Non-asbestos product without pollution
? Good process performance
Silica fiberglass needled mat
Made from silica fiberglass chopped strand through carding and needling process. Fiberglass randomly distributed in 3-D structure. It has properties of small small needling hole and high porosity. It widely used as filtration and high temperature insulation material in coom, steel, nonferrous metal and chemical industry. It also used as acoustic, insulation, damping and fire resistant material in motorcycle and automobile industry.
Specification of silica fiberglass needled mat
Style Thickness
mm Width
cm Weight
g/m2 Breaking strength
N/25×100mm thermal shrinkage % SiO2 content
% remark
Warp Weft
J-SNM1/4” 6.3 7.9 91.5-92 890±80 ≥15 ≥10 ≤13.0 ≥96 Base mat
J-SNM1/2” 12.7 15.9 91.5-92 2000±200 ≥40 ≥20 ≤13.0 ≥96 Base mat
J-SNM1” 21-24 91.5-92 3660±360 ≥80 ≥40 ≤13.0 ≥96 Base mat
remark test condition of thermal shrinkage 980℃ 30 minutes
高硅氧玻璃纤维布具有强度高、易加工、用途广的特点，用作耐高温、耐烧蚀、隔热、保温材料。产品厚度0.1mm-1.5mm，并可根据用户要求进行表面涂覆处理等。
(2) 产品技术指标
产品代号 公称厚度 mm 宽度 cm SiO2含量 % 热失量 % 组织
BWT100 0.10 80~90 ≥96 ≤3 平纹
BWT260 0.26 平纹
BWT600 0.72 80~1200 缎纹
BWT1250 1.35 缎纹
? SiO2≥96%
? Soft point nearly 1700℃, long-period service at 900℃
? Low thermal conductivity
? Good chemical stability
? Good electrical insulation
? Low thermal shrinkage
? Non-asbestos product without pollution
? Good process performance
Silica fiberglass needled mat
Made from silica fiberglass chopped strand through carding and needling process. Fiberglass randomly distributed in 3-D structure. It has properties of small small needling hole and high porosity. It widely used as filtration and high temperature insulation material in coom, steel, nonferrous metal and chemical industry. It also used as acoustic, insulation, damping and fire resistant material in motorcycle and automobile industry.
Specification of silica fiberglass needled mat
Style Thickness
mm Width
cm Weight
g/m2 Breaking strength
N/25×100mm thermal shrinkage % SiO2 content
% remark
Warp Weft
J-SNM1/4” 6.3 7.9 91.5-92 890±80 ≥15 ≥10 ≤13.0 ≥96 Base mat
J-SNM1/2” 12.7 15.9 91.5-92 2000±200 ≥40 ≥20 ≤13.0 ≥96 Base mat
J-SNM1” 21-24 91.5-92 3660±360 ≥80 ≥40 ≤13.0 ≥96 Base mat
remark test condition of thermal shrinkage 980℃ 30 minutes