Standard Test Method for Thermal Diffusivity by the Flash Method

This standard is issued under the fixed designation E 1461; the number immediately following the designation indicates the year of

original adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. A

super epsilon (e) indicates an editorial change since the last revision or reapproval.

1. Scope

1.1 This test method covers the determination of the thermal

diffusivity of primarily homogeneous isotropic solid materials.

Thermal diffusivity values ranging from 10-7 to 10-3 m2/s are

readily measurable by this test method from about 75 to

2800 K.

1.2 This test method is a more detailed form of Test Method

C 714, but has applicability to much wider ranges of materials,

applications, and temperatures, with improved accuracy of

measurements.

1.3 This test method is applicable to the measurements

performed on materials opaque to the spectrum of the energy

pulse, but with special precautions can be used on fully or

partially transparent materials (see Appendix X1).

1.4 This test method is intended to allow a wide variety of

apparatus designs. It is not practical in a test method of this

type to establish details of construction and procedures to cover

all contingencies that might offer difficulties to a person

without pertinent technical knowledge, or to stop or restrict

research and development for improvements in the basic

technique.

1.5 This test method is applicable to the measurements

performed on essentially fully dense materials; however, in

some cases it has shown to produce acceptable results when

used with porous samples. Since the magnitude of porosity,

pore shapes, sizes and parameters of pore distribution influence

the behavior of the thermal diffusivity, extreme caution must be

exercised when analyzing data. Special caution is advised

when other properties, such as thermal conductivity, are

derived from thermal diffusivity obtained by this method.

1.6 This test method can be considered an absolute (or

primary) method of measurement, since no reference standards

are required. It is advisable to use reference materials to verify

the performance of the instrument used.