厂商 :安徽省凤形耐磨材料股份有限公司电子商务中心
安徽 宣城- 主营产品:
- 高铬锻
- 高铬球
- 锤子
化学成份、机械性能、金相组织
序号 |
种类 |
牌号 |
化学成份 |
机械性能 |
金相组织 |
||||||||||
C |
Si |
Mn |
Cr |
Mo |
Ni |
Cu |
S |
P |
Ak (J/cm2) |
HRC |
σb (Mpa) |
||||
1 |
中碳中铬Ⅰ |
ZG30Cr5MoRE |
0.25-0.35 |
0.3-1.0 |
0.3-1.0 |
4.5-5.5 |
0.2-1.0 |
|
|
≤0.045 |
≤0.045 |
≥25 |
≥45 |
|
M+B+C |
2 |
中碳中铬Ⅱ |
ZG40Cr5MoRE |
0.35-0.45 |
0.3-1.0 |
0.3-1.0 |
4.5-5.5 |
0.2-1.0 |
|
|
≤0.045 |
≤0.045 |
≥20 |
≥48 |
|
M+B+C |
3 |
中碳低合金 |
ZG40CrMoNiRE |
0.3-0.5 |
0.7-1.5 |
0.3-1.0 |
1.2-1.8 |
0.2-0.6 |
0.1-0.4 |
|
≤0.04 |
≤0.04 |
≥30 |
≥40 |
|
M+F |
4 |
低碳高合金 |
ZG20Cr9NiMo |
0.15-3.5 |
≤1.0 |
0.3-1.0 |
8-10 |
0.4-0.8 |
1.4-1.8 |
≤0.1 |
≤0.045 |
≤0.045 |
≥40 |
≥40 |
|
M+C |
5 |
铬钼镍合金钢 |
ZG45Cr3NiMoMn-RE |
0.4-0.50 |
0.3-0.8 |
0.6-1.2 |
2.0-3.2 |
0.3-0.5 |
0.5-1.0 |
|
≤0.04 |
≤0.04 |
≥20 |
≥50 |
|
M+C |
6 |
90铬合金钢 |
ZG90Cr6MoMn |
0.85-0.95 |
0.4-0.8 |
0.4-0.8 |
5-8 |
0.2-0.4 |
|
|
≤0.045 |
≤0.045 |
≥7 |
≥50 |
|
M+C |
7 |
普通高猛钢 |
ZGMn13 |
1.1-1.4 |
0.3-1.0 |
11-14 |
|
|
|
|
≤0.06 |
≤0.10 |
≥147 |
HB ≤229 |
637 |
A+C |
8 |
改性高锰钢 |
ZGMn13Cr2 |
1.1-1.4 |
0.3-1.0 |
11-14 |
0.5-2.5 |
|
|
|
≤0.06 |
≤0.10 |
≥80 |
≤240 |
|
A+C |
9 |
超高锰钢 |
ZGMn17Cr2 |
1.1-1.4 |
0.3-1.0 |
16-19 |
1.0-2.0 |
|
Ti0.2-0.4 |
|
≤0.06 |
≤0.10 |
≥50 |
≤260 |
|
A+C |
10 |
耐热钢 |
ZG20Cr26Ni5 |
≤0.20 |
≤2.0 |
≤0.2 |
24-28 |
≤0.5 |
4-6 |
|
≤0.04 |
≤0.04 |
|
|
590 |
A+F |
11 |
HH |
ZG20Cr26Ni12 |
0.2-0.5 |
≤2.0 |
≤0.2 |
24-28 |
≤0.5 |
11-14 |
|
≤0.045 |
≤0.045 |
|
|
490 |
A+F |
12 |
HK |
ZG40Cr25Ni20 |
0.35-0.45 |
≤2.0 |
≤0.2 |
23-27 |
≤0.5 |
19-22 |
|
≤0.045 |
≤0.045 |
|
|
440 |
A+F |
13 |
高铬铸铁 |
KmTBCr15Mo2 |
2-2.8 |
≤1.2 |
0.5-1.0 |
13-18 |
0.2-2.5 |
0-1.0 |
0-1.2 |
≤0.06 |
≤0.10 |
|
≥53 |
|
M+A+C |
14 |
高铬铸铁 |
KmTBCr20Mo2 |
2-3.0 |
≤1.2 |
0.5-1.0 |
18-22 |
1.5-2.5 |
0-1.5 |
0.8-1.2 |
≤0.06 |
≤0.10 |
≥3 |
≥58 |
|
M+A+C |
15 |
高铬铸铁 |
KmTBCr26 |
2-3.0 |
≤1.2 |
0.5-1.0 |
23-28 |
0-1.0 |
0-1.5 |
0-2.0 |
≤0.06 |
≤0.10 |
|
≥55 |
|
M+A+C |
16 |
高铬铸钢 |
ZGCr12SiMn-GT |
1.0-2.0 |
≤1.2 |
0.5-2.0 |
12-14 |
0-1.0 |
0-1.0 |
0-1.0 |
≤0.06 |
≤0.10 |
≥3.2 |
≥55 |
|
M+A+C |
17 |
高铬铸钢 |
ZGCr15SiMn-GT |
1.0-2.0 |
≤1.2 |
0.5-2.0 |
15-17 |
0-1.0 |
0-1.0 |
0-1.0 |
≤0.06 |
≤0.10 |
≥3.5 |
≥55 |
|
M+A+C |