CAMPUS? datasheet | Zytel? 101L NC010
This datasheet of Zytel? 101L NC010 from DuPont Engineering Polymers is provided by the international plastics database CAMPUS.
Zytel? 101L NC010 | PA66 | DuPont Engineering Polymers
Product Texts
ISO 1874-PA66,MGNS,14-030
Common features of Zytel? nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel? nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel? nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel? nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel? nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel? 101L is a lubricated general-purpose polyamide 66 for injection molding.
consumer goods, housings, cable clips, fasteners, connectors.
Common features of Zytel? nylon resin include mechanical and physical properties such as high mechanical strength, excellent balance of stiffness and toughness, good high temperature performance, good electrical and flammability properties, good abrasion and chemical resistance. In addition, Zytel? nylon resins are available in different modified and reinforced grades to create a wide range of products with tailored properties for specific processes and end-uses. Zytel? nylon resin, including most flame retardant grades, offer the ability to be coloured.
The good melt stability of Zytel? nylon resin normally enables the recycling of properly handled production waste. If recycling is not possible, DuPont recommends, as the preferred option, incineration with energy recovery (-31kJ/g of base polymer) in appropriately equipped installations. For disposal, local regulations have to be observed.
Zytel? nylon resin typically is used in demanding applications in the automotive, furniture, domestic appliances, sporting goods and construction industry.
Zytel? 101L is a lubricated general-purpose polyamide 66 for injection molding.
Food compliance:
Specific statement for EU availableTypical applications:
Parts with medium to high wall thickness, mechanical components andconsumer goods, housings, cable clips, fasteners, connectors.
| Rheological properties | dry / cond | Unit | Test Standard |
| Molding shrinkage, parallel | 1.3 / * | % | ISO 294-4, 2577 |
| Molding shrinkage, normal | 1.3 / * | % | ISO 294-4, 2577 |
| Mechanical properties | dry / cond | Unit | Test Standard |
| Tensile Modulus | 3000 / 1400 | MPa | ISO 527-1/-2 |
| Yield stress | 82 / 53 | MPa | ISO 527-1/-2 |
| Yield strain | 4.5 / 25 | % | ISO 527-1/-2 |
| Nominal strain at break | 25 / >50 | % | ISO 527-1/-2 |
| Tensile creep modulus, 1h | * / 1200 | MPa | ISO 899-1 |
| Tensile creep modulus, 1000h | * / 700 | MPa | ISO 899-1 |
| Charpy impact strength, +23°C | N / N | kJ/m? | ISO 179/1eU |
| Charpy impact strength, -30°C | 400 / N | kJ/m? | ISO 179/1eU |
| Charpy notched impact strength, +23°C | 5.5 / 15 | kJ/m? | ISO 179/1eA |
| Charpy notched impact strength, -30°C | 4.5 / 4 | kJ/m? | ISO 179/1eA |
| Thermal properties | dry / cond | Unit | Test Standard |
| Melting temperature, 10°C/min | 263 / * | °C | ISO 11357-1/-3 |
| Glass transition temperature, 10°C/min | 60 / * | °C | ISO 11357-1/-2 |
| Temp. of deflection under load, 1.80 MPa | 70 / * | °C | ISO 75-1/-2 |
| Temp. of deflection under load, 0.45 MPa | 200 / * | °C | ISO 75-1/-2 |
| Vicat softening temperature, 50°C/h 50N | 240 / * | °C | ISO 306 |
| Coeff. of linear therm. expansion, parallel | 100 / * | E-6/K | ISO 11359-1/-2 |
| Coeff. of linear therm. expansion, normal | 110 / * | E-6/K | ISO 11359-1/-2 |
| Burning Behav. at 1.5 mm nom. thickn. | V-2 / * | class | IEC 60695-11-10 |
| Thickness tested | 1.5 / * | mm | IEC 60695-11-10 |
| UL recognition | UL / * | - | - |
| Burning Behav. at thickness h | V-2 / * | class | IEC 60695-11-10 |
| Thickness tested | 0.4 / * | mm | IEC 60695-11-10 |
| UL recognition | UL / * | - | - |
| Oxygen index | 28 / * | % | ISO 4589-1/-2 |
| Electrical properties | dry / cond | Unit | Test Standard |
| Relative permittivity, 100Hz | 3.8 / 6 | - | IEC 60250 |
| Relative permittivity, 1MHz | 3.5 / 4 | - | IEC 60250 |
| Dissipation factor, 100Hz | 80 / 2100 | E-4 | IEC 60250 |
| Dissipation factor, 1MHz | 180 / 750 | E-4 | IEC 60250 |
| Volume resistivity | 1E12 / 1E10 | Ohm*m | IEC 60093 |
| Surface resistivity | * / 1E12 | Ohm | IEC 60093 |
| Electric strength | 32 / 28 | kV/mm | IEC 60243-1 |
| Comparative tracking index | 600 / - | - | IEC 60112 |
| Other properties | dry / cond | Unit | Test Standard |
| Water absorption | 8.5 / * | % | Sim. to ISO 62 |
| Humidity absorption | 2.6 / * | % | Sim. to ISO 62 |
| Density | 1140 / - | kg/m? | ISO 1183 |
| Material specific properties | dry / cond | Unit | Test Standard |
| Viscosity number | 150 / * | cm?/g | ISO 307, 1157, 1628 |
| Film Properties | dry / cond | Unit | Test Standard |
| Strain at yield, parallel | 4.5 / * | % | ISO 527-3 |
| Rheological calculation properties | Value | Unit | Test Standard |
| Density of melt | 970 | kg/m? | - |
| Thermal conductivity of melt | 0.16 | W/(m K) | - |
| Spec. heat capacity of melt | 2790 | J/(kg K) | - |
| Eff. thermal diffusivity | 5E-8 | m?/s | - |
| Ejection temperature | 190 | °C | - |
Diagrams
Characteristics
Processing
Injection Molding
Delivery form
Pellets
Additives
Release agent
Regional Availability
North America, Europe, Asia Pacific, South and Central America, Near East/Africa
Other text information
Injection molding
PREPROCESSING
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 290°C
Melt temperature range = 280-300°C
Mold temperature optimum = 70°C
Mold temperature range = 50-90°C
Maximum Screw tangential Speed : 0.4 m/s
Flow front speed : 300 m m/s
Hold pressure optimum : 85 MPa
Hold pressure range : 50-100 MPa
Back pressure : low
Hold pressure time : 4 s/mm
Maximum hold-up time : 15 min
Moulding guide
POSTPROCESSING
Annealing: 30min at 200°C
Drying recommended = Yes, if moisture content of resin exceeds recommended level
Drying temperature = 80°C
Drying time, dehumidified dryer = 2-4 h
Processing moisture content = <0.2 %
PROCESSING
Melt temperature optimum = 290°C
Melt temperature range = 280-300°C
Mold temperature optimum = 70°C
Mold temperature range = 50-90°C
Maximum Screw tangential Speed : 0.4 m/s
Flow front speed : 300 m m/s
Hold pressure optimum : 85 MPa
Hold pressure range : 50-100 MPa
Back pressure : low
Hold pressure time : 4 s/mm
Maximum hold-up time : 15 min
Moulding guide
POSTPROCESSING
Annealing: 30min at 200°C
Chemical Media Resistance
| Acids | |
 |
Acetic Acid (5% by mass) (23°C) |
|
Citric Acid solution (10% by mass) (23°C) |
|
Lactic Acid (10% by mass) (23°C) |
 |
Hydrochloric Acid (36% by mass) (23°C) |
|
Nitric Acid (40% by mass) (23°C) |
|
Sulfuric Acid (38% by mass) (23°C) |
|
Sulfuric Acid (5% by mass) (23°C) |
|
Chromic Acid solution (40% by mass) (23°C) |
| Bases | |
|
Sodium Hydroxide solution (35% by mass) (23°C) |
|
Sodium Hydroxide solution (1% by mass) (23°C) |
|
Ammonium Hydroxide solution (10% by mass) (23°C) |
| Alcohols | |
|
Isopropyl alcohol (23°C) |
|
Methanol (23°C) |
|
Ethanol (23°C) |
| Hydrocarbons | |
|
n-Hexane (23°C) |
|
Toluene (23°C) |
|
iso-Octane (23°C) |
| Ketones | |
|
Acetone (23°C) |
| Ethers | |
|
Diethyl ether (23°C) |
| Mineral oils | |
|
SAE 10W40 multigrade motor oil (23°C) |
|
SAE 10W40 multigrade motor oil (130°C) |
|
SAE 80/90 hypoid-gear oil (130°C) |
|
Insulating Oil (23°C) |
| Standard Fuels | |
|
ISO 1817 Liquid 1 (60°C) |
|
ISO 1817 Liquid 2 (60°C) |
|
ISO 1817 Liquid 3 (60°C) |
|
ISO 1817 Liquid 4 (60°C) |
|
Standard fuel without alcohol (pref. ISO 1817 Liquid C) (23°C) |
|
Standard fuel with alcohol (pref. ISO 1817 Liquid 4) (23°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (23°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (90°C) |
|
Diesel fuel (pref. ISO 1817 Liquid F) (>90°C) |
| Salt solutions | |
|
Sodium Chloride solution (10% by mass) (23°C) |
|
Sodium Hypochlorite solution (10% by mass) (23°C) |
|
Sodium Carbonate solution (20% by mass) (23°C) |
|
Sodium Carbonate solution (2% by mass) (23°C) |
|
Zinc Chloride solution (50% by mass) (23°C) |
| Other | |
|
Ethyl Acetate (23°C) |
|
Hydrogen peroxide (23°C) |
|
DOT No. 4 Brake fluid (130°C) |
|
Ethylene Glycol (50% by mass) in water (108°C) |
|
1% nonylphenoxy-polyethyleneoxy ethanol in water (23°C) |
|
50% Oleic acid + 50% Olive Oil (23°C) |
|
Water (23°C) |
|
Deionized water (90°C) |
|
Phenol solution (5% by mass) (23°C) |