②原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 物理性能 |
比重 |
--- |
ASTM D-792 |
1.2 |
--- |
| 模具收缩率 |
3.2mm |
ASTM D-955 |
5-7 |
10-3 |
| 熔体流动速率 |
--- |
ASTM D-1238 |
3.5 |
g/10min |
| 机械性能 |
拉伸强度 |
屈伏点 |
ASTM D-638 |
62 |
MPa |
| 拉伸率 |
断裂点 |
ASTM D-638 |
110 |
% |
| 弯曲强度 |
--- |
ASTM D-790 |
93 |
MPa |
| 弯曲模量 |
--- |
ASTM D-790 |
2343 |
MPa |
| 冲击强度 |
缺口23℃ |
ASTM D-256 |
907 |
J/M |
| 洛氏硬度 |
R |
ASTM D-785 |
118 |
--- |
| 冲击强度 |
缺口23℃ |
ASTM D-256 |
907 |
J/M |
| 电气性能 |
损耗因数 |
60Hz |
ASTM D-150 |
0.0009 |
--- |
| 损耗因数 |
1MHz |
ASTM D-150 |
0.01 |
--- |
| 介电常数 |
60Hz |
ASTM D-150 |
3.17 |
--- |
| 体积电阻 |
--- |
ASTM D-257 |
1×1017 |
Ω.cm |
| 加工性能 |
吸水率 |
--- |
ASTM D-570 |
0.15 |
% |
| 热 性 能 |
热变形温度 |
0.45MPa |
ASTM D-648 |
137 |
℃ |
| 热变形强度 |
0.45MPa |
ASTM D-648 |
137 |
℃ |
| 热变形温度 |
1.8MPa |
ASTM D-648 |
132 |
℃ |
| 维卡软化点 |
--- |
ASTM D-1525 |
154 |
℃ |
| 线膨胀系数 |
--- |
ASTM E-831 |
6.8×10-5 |
1/℃ |
| UL 长期使用温度 |
--- |
UL 746B |
115 |
℃ |
| 阻燃性 |
--- |
UL 94 |
HB |
--- | | | | | | |