比重
|
1.79 g/cc
|
1.79 g/cc
|
ASTM D792
|
|
密度
|
1.79 g/cc
|
0.0647 lb/in?
|
ISO 1183
|
|
填料含量
|
43 %
|
43 %
|
|
|
Water Absorption
|
0.060 %
@Temperature 23.0 °C
|
0.060 %
@Temperature 73.4 °F
|
50%RH,23°C,24h; ASTM D570
|
|
0.11 %
@Temperature 23.0 °C
|
0.11 %
@Temperature 73.4 °F
|
E 50%RH; ISO 62, Similar to
|
|
0.62 %
@Temperature 23.0 °C
|
0.62 %
@Temperature 73.4 °F
|
Saturation, immersed; ISO 62, Similar to
|
|
线性成型收缩率
|
0.0013 cm/cm
@Thickness 1.57 mm
|
0.0013 in/in
@Thickness 0.0618 in
|
Flow
|
|
0.0020 cm/cm
@Thickness 3.20 mm
|
0.0020 in/in
@Thickness 0.126 in
|
Flow
|
|
0.0048 cm/cm
@Thickness 1.57 mm
|
0.0048 in/in
@Thickness 0.0618 in
|
Transverse
|
|
0.0065 cm/cm
@Thickness 3.20 mm
|
0.0065 in/in
@Thickness 0.126 in
|
Transverse
|
|
线性成型收缩率,Flow
|
0.0025 cm/cm
|
0.0025 in/in
|
Annealed; ISO 294-4
|
|
0.0020 cm/cm
@Thickness 2.00 mm
|
0.0020 in/in
@Thickness 0.0787 in
|
ISO 294-4
|
|
线性成型收缩率，横向
|
0.0105 cm/cm
|
0.0105 in/in
|
Annealed; ISO 294-4
|
|
0.0075 cm/cm
@Thickness 2.00 mm
|
0.0075 in/in
@Thickness 0.0787 in
|
ISO 294-4
|
|
化合物熔体指数
|
6.0 g/10 min
@Load 2.16 kg, Temperature 280 °C
|
6.0 g/10 min
@Load 4.76 lb, Temperature 536 °F
|
cm3/10 min; ISO 1133
|