POLIMID A SG NATURAL Y
非填充-加二硫化钼润滑
PA66 UNFILLED-LUBRICATED WITH MOLYBDENUM DISULFIDE
|
|
特性 |
|
标准 |
|
单位 |
|
典型值 |
|
||||
|
|
Properties |
|
Standard |
|
Unit |
|
Typical Values |
|
||||
|
物理和热/ PHYSICAL & THERMAL |
|
|
|
|
|
|
|
|
|
|
||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
密度 |
|
|
ISO 1183 |
|
g/cm? |
|
|
1.14 |
|
|
|
|
|
Density |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
熔点 |
|
|
DSC |
|
°C |
|
260 |
|
|
|
||
|
Melting Point |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
成型收缩率 (均值) |
|
|
- |
|
|
% |
|
|
1.4 – 1.8 |
|
|
|
|
Mold Shrinkage (average) |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
吸湿率 (浸水) |
|
23oC - 24h |
ISO 62 |
% |
|
|
1.2 |
|
|
|
||
|
Moisture Absorption (water immersion) |
|
|
|
|
|
|||||||
|
熔流指数 |
|
|
ISO 1133 |
|
g/10min |
|
|
- |
|
|
|
|
|
Melt Flow Index |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
维卡软化温度 |
|
|
ISO 306 |
|
°C |
|
255 |
|
|
|
||
|
Vicat Softening Temperature |
|
50°C/h - 10 N |
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
热变形温度 |
|
|
ISO 75-2 |
|
°C |
|
|
212 |
|
|
|
|
|
Heat Deflection Temperature |
|
0,45 MPa |
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
热变形温度 |
|
1,80 MPa |
ISO 75-2 |
|
°C |
|
93 |
|
|
|
||
|
Heat Deflection Temperature |
|
|
|
|
|
|
||||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
耐热/球压测试 |
|
|
IEC 335-1 |
|
°C |
|
|
> 165 |
|
|
|
|
|
Heat Resistance / Ball test |
|
|
IEC 60695-10-2 |
|
|
|
|
|
|
|||
|
|
|
|
|
|
|
|
|
|
|
|||
|
连续使用温度(无负载) |
|
|
- |
|
|
°C |
|
90 |
|
|
|
|
|
Continuous Use Temperature (without load) |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
机械 / MECHANICAL |
|
|
|
|
|
|
|
|
|
|
|
|
|
屈服拉伸强度 |
|
|
ISO 527 |
|
MPa |
|
|
90 |
|
|
|
|
|
Tensile Strength at Yield |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
断裂拉伸强度 |
|
|
ISO 527 |
|
MPa |
|
- |
|
|
|
||
|
Tensile Strength at Break |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
拉伸模量 |
|
|
ISO 527 |
|
MPa |
|
|
3250 |
|
|
|
|
|
Tensile Modulus |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
屈服拉伸应变 |
|
|
ISO 527 |
% |
|
|
4.5 |
|
|
|
||
|
Tensile Strain at Yield |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
断裂拉伸应变 |
|
|
ISO 527 |
|
% |
|
|
15 |
|
|
|
|
|
Tensile Strain at Break |
|
|
|
|
|
|
|
|
||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
悬挂梁缺口冲击强度 |
|
|
ISO 180/A |
|
KJ/ m? |
|
4.5 |
|
|
|
||
|
Izod - Notched Impact Strength |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
悬挂梁无缺口冲击强度 |
|
|
ISO 180/U |
|
KJ/m? |
|
|
- |
|
|
|
|
|
Izod - Unnotched Impact Strength |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
电气和可燃性 / ELECTRICAL & FLAME RETARDANCY |
|
|
|
|
|
|
|
|
||||
|
相对起痕指数 (CTI) |
|
|
IEC 60112 |
|
V |
|
|
>600 |
|
|
|
|
|
Comparative Tracking Index (CTI) |
|
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
可燃性 |
|
|
UL 94 |
- |
|
|
HB |
|
||||
|
Flammability |
|
3,2 /1,6 / 0,8 mm |
|
|
|
|||||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
灼热丝可燃性温度 (GWIT) |
|
|
IEC 60695-2-12 |
|
°C |
|
|
- |
|
|
|
|
|
Glow Wire Flammability Temperature |
GWFI - 2 mm |
|
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|||
|
灼热丝起燃性温度 (GWIT) |
|
|
IEC 60695-2-13 |
|
°C |
|
- |
|
|
|
||
|
Glow Wire Ignition Temperature |
|
GWIT - 2 mm |
|
|
|
|
|
|||||
|
|
|
|
|
|
|
|
|
|
|
|
||
|
|
成型条件 (建议) / Molding conditions (suggested) |
|
|
|
|
|
|
|
|
|||
|
干燥温度 |
≥ 3 h / 90 - 100 oC |
成型温度 |
260 - 280 oC |
|
模具温度 |
70 - 90 oC |
|
|
|
|||
|
Drying Temperature |
Molding temperature |
|
Mold temperature |
|
|
|
- PC-PBT. 2230 XENOY™.聚碳酸酯聚对苯二甲酸丁二醇酯
- PA612.EMS CR 9.聚酰胺612.尼龙.Grilon®
- PBT.LW9320.polybutylene terephthalate
- LCP.VECTRA® E130.LIQUID CRYSTAL POLYMER.液晶聚合物.高分子材料
- LG ASA LI-912.913.丙烯酸酯类橡胶体与丙烯腈、苯乙烯
- 基础创新塑料LNP™LUBRICOMP™PC DBL-4034 BK.DBL34.聚碳酸酯
- PC TRIREX®3025G10.聚碳酸酯. PC塑料.Polycarbonate
- Santoprene™ 埃克森美孚TPV 121-65M300.热塑性硫化橡胶.Thermoplastic Vulcan
- Delrin® 500P POM 500 POM Delrin® 500
- 赫斯特Hostaform® POM.M90AXP.聚甲醛.超钢.赛钢 POM.M90AXP.C9021