商品详细描述

供应30％玻纤增强PC脱模3433R

30% GR, provides improved mechanical properties. UV-stabilized. Internal mold release.
 
 
TYPICAL PROPERTIES (1)
MECHANICAL Value Unit Standard
Tensile Stress, brk, Type I, 5 mm/min 1330 kgf/cm? ASTM D 638
Tensile Strain, brk, Type I, 5 mm/min 3 % ASTM D 638
Flexural Stress, yld, 1.3 mm/min, 50 mm span 1610 kgf/cm? ASTM D 790
Flexural Modulus, 1.3 mm/min, 50 mm span 77300 kgf/cm? ASTM D 790
Hardness, Rockwell M 92 - ASTM D 785
Hardness, Rockwell R 121 - ASTM D 785
Taber Abrasion, CS-17, 1 kg 24 mg/1000cy ASTM D 1044
IMPACT Value Unit Standard
Izod Impact, unnotched, 23°C 114 cm-kgf/cm ASTM D 4812
Izod Impact, notched, 23°C 10 cm-kgf/cm ASTM D 256
Tensile Impact, Type S 68 cm-kgf/cm? ASTM D 1822
Falling Dart Impact (D 3029), 23°C 55 cm-kgf ASTM D 3029
THERMAL Value Unit Standard
Vicat Softening Temp, Rate B/50 154 °C ASTM D 1525
HDT, 0.45 MPa, 6.4 mm, unannealed 151 °C ASTM D 648
HDT, 1.82 MPa, 6.4 mm, unannealed 146 °C ASTM D 648
CTE, -40°C to 95°C, flow 2.16E-05 1/°C ASTM E 831
Specific Heat 1.13 J/g-°C ASTM C 351
Thermal Conductivity 0.22 W/m-°C ASTM C 177
PHYSICAL Value Unit Standard
Specific Gravity 1.43 - ASTM D 792
Specific Volume 0.69 cm?/g ASTM D 792
Density 1.439 g/cm? ASTM D 792
Water Absorption, 24 hours 0.14 % ASTM D 570
Water Absorption, equilibrium, 23C 0.26 % ASTM D 570
Mold Shrinkage, flow, 3.2 mm (5) 0.1 - 0.3 % SABIC Method
Melt Flow Rate, 300°C/5.0 kgf 19 g/10 min ASTM D 1238
Parameter
Injection Molding Value Unit
Drying Temperature 120 °C
Drying Time 3 - 4 hrs
Drying Time (Cumulative) 48 hrs
Maximum Moisture Content 0.02 %
Melt Temperature 315 - 340 °C
Nozzle Temperature 310 - 330 °C
Front - Zone 3 Temperature 315 - 340 °C
Middle - Zone 2 Temperature 305 - 325 °C
Rear - Zone 1 Temperature 295 - 315 °C
Mold Temperature 80 - 115 °C
Back Pressure 0.3 - 0.7 MPa
Screw Speed 40 - 70 rpm
Shot to Cylinder Size 40 - 60 %
Vent Depth 0.025 - 0.076 mm