商品详细描述
美
国沙伯PC聚碳酸酯阻燃抗UV级
201 阻燃。201R 阻燃 脱模剂。203 阻燃，抗UV。203R 阻燃 抗UV，脱模剂。221 阻燃。221R 阻燃 脱模剂。223 阻燃，抗UV。223R 阻燃，抗UV，脱模剂。241 阻燃。241R 阻燃 脱模剂。243 阻燃，抗UV。243R 阻燃，抗UV，脱模剂。244R 可电镀。
增强阻燃级
3412ECR 20％玻纤增强，阻燃。3412R 20％玻纤增强，阻燃。
LEXAN ? Resin 3412ECR |
|
|
|
|
|
| LEXAN 3412ECR Polycarbonate (PC) resin is a 20% glass fiber filled, injection moldable grade. This non-chlorinated, non-brominated flame retardant GF-PC has an UL-94 V0 rating and is available in various opaque color options. LEXAN 3412ECR is a resin designed to meet the needs of high stiffness applications. |
| TYPICAL PROPERTIES (1) | ||||
| MECHANICAL | Value | Unit | Standard | |
| Tensile Stress, yld, Type I, 5 mm/min | 910 | kgf/cm? | ASTM D 638 | |
| Tensile Stress, brk, Type I, 5 mm/min | 880 | kgf/cm? | ASTM D 638 | |
| Tensile Strain, yld, Type I, 5 mm/min | 3.1 | % | ASTM D 638 | |
| Tensile Modulus, 5 mm/min | 56000 | kgf/cm? | ASTM D 638 | |
| Flexural Stress, yld, 1.3 mm/min, 50 mm span | 1590 | kgf/cm? | ASTM D 790 | |
| Flexural Modulus, 1.3 mm/min, 50 mm span | 50900 | kgf/cm? | ASTM D 790 | |
| Tensile Stress, yield, 5 mm/min | 95 | MPa | ISO 527 | |
| Tensile Stress, break, 5 mm/min | 90 | MPa | ISO 527 | |
| Tensile Strain, yield, 5 mm/min | 2.8 | % | ISO 527 | |
| Tensile Strain, break, 5 mm/min | 3.2 | % | ISO 527 | |
| Tensile Modulus, 1 mm/min | 6000 | MPa | ISO 527 | |
| Flexural Stress, yield, 2 mm/min | 140 | MPa | ISO 178 | |
| Flexural Modulus, 2 mm/min | 5500 | MPa | ISO 178 | |
| IMPACT | Value | Unit | Standard | |
| Izod Impact, notched, 23°C | 11 | cm-kgf/cm | ASTM D 256 | |
| Izod Impact, notched, -30°C | 10 | cm-kgf/cm | ASTM D 256 | |
| Instrumented Impact Total Energy, 23°C | 203 | cm-kgf | ASTM D 3763 | |
| Izod Impact, unnotched 80*10*3 +23°C | 35 | kJ/m? | ISO 180/1U | |
| Izod Impact, unnotched 80*10*3 -30°C | 35 | kJ/m? | ISO 180/1U | |
| Izod Impact, notched 80*10*3 +23°C | 7 | kJ/m? | ISO 180/1A | |
| Izod Impact, notched 80*10*3 -30°C | 6 | kJ/m? | ISO 180/1A | |
| Charpy 23°C, V-notch Edgew 80*10*3 sp=62mm | 6 | kJ/m? | ISO 179/1eA | |
| Charpy -30°C, V-notch Edgew 80*10*3 sp=62mm | 5 | kJ/m? | ISO 179/1eA | |
| Charpy 23°C, Unnotch Edgew 80*10*3 sp=62mm | 40 | kJ/m? | ISO 179/1eU | |
| Charpy -30°C, Unnotch Edgew 80*10*3 sp=62mm | 40 | kJ/m? | ISO 179/1eU | |
| THERMAL | Value | Unit | Standard | |
| Vicat Softening Temp, Rate B/50 | 147 | °C | ASTM D 1525 | |
| HDT, 1.82 MPa, 3.2mm, unannealed | 141 | °C | ASTM D 648 | |
| CTE, -40°C to 40°C, flow | 3.E-05 | 1/°C | ASTM E 831 | |
| CTE, -40°C to 40°C, xflow | 7.E-05 | 1/°C | ASTM E 831 | |
| CTE, 23°C to 80°C, flow | 3.E-05 | 1/°C | ISO 11359-2 | |
| CTE, 23°C to 80°C, xflow | 7.E-05 | 1/°C | ISO 11359-2 | |
| Ball Pressure Test, 125°C +/- 2°C | PASSES | - | IEC 60695-10-2 | |
| Vicat Softening Temp, Rate B/50 | 145 | °C | ISO 306 | |
| Vicat Softening Temp, Rate B/120 | 146 | °C | ISO 306 | |
| HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm | 141 | °C | ISO 75/Bf | |
| HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm | 136 | °C | ISO 75/Af | |
| Relative Temp Index, Elec | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/impact | 130 | °C | UL 746B | |
| Relative Temp Index, Mech w/o impact | 130 | °C | UL 746B | |
| PHYSICAL | Value | Unit | Standard | |
| Specific Gravity | 1.3 | - | ASTM D 792 | |
| Mold Shrinkage, flow, 3.2 mm (5) | 0.2 - 0.5 | % | SABIC Method | |
| Mold Shrinkage, xflow, 3.2 mm (5) | 0.2 - 0.5 | % | SABIC Method | |
| Melt Flow Rate, 300°C/1.2 kgf | 7 | g/10 min | ASTM D 1238 | |
| Density | 1.36 | g/cm? | ISO 1183 | |
| Water Absorption, (23°C/sat) | 0.29 | % | ISO 62 | |
| Moisture Absorption (23°C / 50% RH) | 0.12 | % | ISO 62 | |
| Melt Volume Rate, MVR at 300°C/1.2 kg | 7 | cm?/10 min | ISO 1133 | |
| ELECTRICAL | Value | Unit | Standard | |
| Arc Resistance, Tungsten {PLC} | 7 | PLC Code | ASTM D 495 | |
| Hot Wire Ignition {PLC) | 0 | PLC Code | UL 746A | |
| High Voltage Arc Track Rate {PLC} | 3 | PLC Code | UL 746A | |
| High Ampere Arc Ign, surface {PLC} | 3 | PLC Code | UL 746A | |
| Comparative Tracking Index (UL) {PLC} | 3 | PLC Code | UL 746A | |
| Volume Resistivity | >1.E+15 | Ohm-cm | IEC 60093 | |
| Surface Resistivity, ROA | >1.E+15 | Ohm | IEC 60093 | |
| Relative Permittivity, 1 MHz | 3.3 | - | IEC 60250 | |
| Dissipation Factor, 50/60 Hz | 0.02 | - | IEC 60250 | |
| Dissipation Factor, 1 MHz | 0.01 | - | IEC 60250 | |
| Relative Permittivity, 50/60 Hz | 3.3 | - | IEC 60250 | |
| FLAME CHARACTERISTICS | Value | Unit | Standard | |
| UL Recognized, 94V-0 Flame Class Rating (3) | 1.5 | mm | UL 94 | |
| UL Recognized, 94-5VA Rating (3) | 3 | mm | UL 94 | |
| Glow Wire Flammability Index 960°C, passes at | 1 | mm | IEC 60695-2-12 | |
| Glow Wire Ignitability Temperature, 1.0 mm | 825 | °C | IEC 60695-2-13 | |
| Oxygen Index (LOI) | 40 | % | ISO 4589 | |
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 120 | °C |
| Drying Time | 3 - 4 | hrs |
| Drying Time (Cumulative) | 48 | hrs |
| Maximum Moisture Content | 0.02 | % |
| Melt Temperature | 290 - 310 | °C |
| Nozzle Temperature | 280 - 305 | °C |
| Front - Zone 3 Temperature | 290 - 310 | °C |
| Middle - Zone 2 Temperature | 275 - 300 | °C |
| Rear - Zone 1 Temperature | 265 - 290 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.3 - 0.7 | MPa |
| Screw Speed | 40 - 70 | rpm |
| Shot to Cylinder Size | 40 - 60 | % |
| Vent Depth | 0.025 - 0.076 |
mm |