TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 0.2 in/min
|
6300
|
psi
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 0.2 in/min
|
4700
|
psi
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 0.2 in/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 0.2 in/min
|
24
|
%
|
ASTM D 638
|
|
Tensile Modulus, 0.2 in/min
|
329000
|
psi
|
ASTM D 638
|
|
Flexural Stress, yld, 0.05 in/min, 2 in span
|
10100
|
psi
|
ASTM D 790
|
|
Flexural Modulus, 0.05 in/min, 2 in span
|
333000
|
psi
|
ASTM D 790
|
|
Hardness, Rockwell R
|
112
|
-
|
ASTM D 785
|
|
Tensile Stress, yield, 50 mm/min
|
47
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 50 mm/min
|
35
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 50 mm/min
|
2.5
|
%
|
ISO 527
|
|
Tensile Strain, break, 50 mm/min
|
25
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2370
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
70
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2200
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 73°F
|
6
|
ft-lb/in
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 73°F
|
265
|
in-lb
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
22
|
kJ/m?
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
8
|
kJ/m?
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
26
|
kJ/m?
|
ISO 179/1eA
|
|
Charpy -30°C, V-notch Edgew 80*10*4 sp=62mm
|
9
|
kJ/m?
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
210
|
°F
|
ASTM D 1525
|
|
HDT, 66 psi, 0.125 in, unannealed
|
201
|
°F
|
ASTM D 648
|
|
HDT, 264 psi, 0.125 in, unannealed
|
176
|
°F
|
ASTM D 648
|
|
CTE, flow, -40°F to 100°F
|
4.9E-05
|
1/°F
|
ASTM E 831
|
|
CTE, xflow, -40°F to 100°F
|
4.9E-05
|
1/°F
|
ASTM E 831
|
|
Vicat Softening Temp, Rate B/50
|
98
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
100
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
81
|
°C
|
ISO 75/Af
|
|
Relative Temp Index, Elec
|
60
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/impact
|
60
|
°C
|
UL 746B
|
|
Relative Temp Index, Mech w/o impact
|
60
|
°C
|
UL 746B
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.04
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 0.125" (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate, 230°C/3.8 kgf
|
5.6
|
g/10 min
|
ASTM D 1238
|
|
Melt Viscosity, 240°C, 1000 sec-1
|
2250
|
poise
|
ASTM D 3825
|
|
Density
|
0.03
|
lb/in?
|
ISO 1183
|
|
Melt Flow Rate, 220°C/10.0 kg
|
18
|
g/10 min
|
ISO 1133
|
|
ELECTRICAL
|
Value
|
Unit
|
Standard
|
|
Arc Resistance, Tungsten {PLC}
|
6
|
PLC Code
|
ASTM D 495
|
|
Hot Wire Ignition {PLC)
|
3
|
PLC Code
|
UL 746A
|
|
High Voltage Arc Track Rate {PLC}
|
3
|
PLC Code
|
UL 746A
|
|
High Ampere Arc Ign, surface {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
Comparative Tracking Index (UL) {PLC}
|
0
|
PLC Code
|
UL 746A
|
|
FLAME CHARACTERISTICS
|
Value
|
Unit
|
Standard
|
|
UL Recognized, 94HB Flame Class Rating (3)
|
0.059
|
in
|
UL 94
|