TYPICAL PROPERTIES (1)
|
|
MECHANICAL
|
Value
|
Unit
|
Standard
|
|
Tensile Stress, yld, Type I, 0.2 in/min
|
6800
|
psi
|
ASTM D 638
|
|
Tensile Stress, brk, Type I, 0.2 in/min
|
5200
|
psi
|
ASTM D 638
|
|
Tensile Strain, yld, Type I, 0.2 in/min
|
2
|
%
|
ASTM D 638
|
|
Tensile Strain, brk, Type I, 0.2 in/min
|
18
|
%
|
ASTM D 638
|
|
Tensile Modulus, 0.2 in/min
|
359000
|
psi
|
ASTM D 638
|
|
Flexural Stress, yld, 0.05 in/min, 2 in span
|
11500
|
psi
|
ASTM D 790
|
|
Flexural Modulus, 0.05 in/min, 2 in span
|
379000
|
psi
|
ASTM D 790
|
|
Tensile Stress, yield, 5 mm/min
|
40
|
MPa
|
ISO 527
|
|
Tensile Stress, break, 5 mm/min
|
35
|
MPa
|
ISO 527
|
|
Tensile Strain, yield, 5 mm/min
|
2
|
%
|
ISO 527
|
|
Tensile Strain, break, 5 mm/min
|
35
|
%
|
ISO 527
|
|
Tensile Modulus, 1 mm/min
|
2450
|
MPa
|
ISO 527
|
|
Flexural Stress, yield, 2 mm/min
|
65
|
MPa
|
ISO 178
|
|
Flexural Modulus, 2 mm/min
|
2500
|
MPa
|
ISO 178
|
|
IMPACT
|
Value
|
Unit
|
Standard
|
|
Izod Impact, notched, 73°F
|
4.5
|
ft-lb/in
|
ASTM D 256
|
|
Izod Impact, notched, -22°F
|
1.4
|
ft-lb/in
|
ASTM D 256
|
|
Instrumented Impact Total Energy, 73°F
|
185
|
in-lb
|
ASTM D 3763
|
|
Izod Impact, notched 80*10*4 +23°C
|
18
|
kJ/m?
|
ISO 180/1A
|
|
Izod Impact, notched 80*10*4 -30°C
|
7
|
kJ/m?
|
ISO 180/1A
|
|
Charpy 23°C, V-notch Edgew 80*10*4 sp=62mm
|
23
|
kJ/m?
|
ISO 179/1eA
|
|
THERMAL
|
Value
|
Unit
|
Standard
|
|
Vicat Softening Temp, Rate B/50
|
210
|
°F
|
ASTM D 1525
|
|
HDT, 66 psi, 0.125 in, unannealed
|
204
|
°F
|
ASTM D 648
|
|
HDT, 264 psi, 0.125 in, unannealed
|
179
|
°F
|
ASTM D 648
|
|
CTE, flow, -40°F to 100°F
|
4.9E-05
|
1/°F
|
ASTM E 831
|
|
CTE, xflow, -40°F to 100°F
|
4.7E-05
|
1/°F
|
ASTM E 831
|
|
CTE, -40°C to 40°C, flow
|
8.8E-05
|
1/°C
|
ISO 11359-2
|
|
CTE, -40°C to 40°C, xflow
|
8.5E-05
|
1/°C
|
ISO 11359-2
|
|
Vicat Softening Temp, Rate B/50
|
99
|
°C
|
ISO 306
|
|
Vicat Softening Temp, Rate B/120
|
100
|
°C
|
ISO 306
|
|
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm
|
82
|
°C
|
ISO 75/Af
|
|
PHYSICAL
|
Value
|
Unit
|
Standard
|
|
Specific Gravity
|
1.04
|
-
|
ASTM D 792
|
|
Mold Shrinkage, flow, 0.125" (5)
|
0.5 - 0.8
|
%
|
SABIC Method
|
|
Melt Flow Rate, 230°C/3.8 kgf
|
11.7
|
g/10 min
|
ASTM D 1238
|
|
Density
|
0.03
|
lb/in?
|
ISO 1183
|
|
Water Absorption, equilibrium, 73°F
|
0.5
|
%
|
ISO 62
|
|
Moisture Absorption (23°C / 50% RH)
|
0.16
|
%
|
ISO 62
|
|
Melt Volume Rate, MVR at 220°C/5.0 kg
|
12
|
cm?/10 min
|
ISO 1133
|